The formation of hard accumulation in senagat gazanlary (stone we mud ) is caused by some impurities we corrosion ÖNÜMLER contained in water. Examples of water impurities are; dissolved calcium, magnesium chloride, sulfate we silicon elements; Examples of corrosion ÖNÜMLER include iron we copper. The water impurities in the senagat gazany consist of condensate leaks we senagat gazany feed water (make-up); Corrosion ÖNÜMLER, as a result of corrosion, also comes from the condensate we feed water

Deposits cause a waste of fuel in the senagat gazany, a slight decrease in Önümivity, we more importantly, overheating occurs metal annealing we pipe explosion. The senagat gazany zone where the accumulation causes the biggest problem is the evaporator pipes around the Gorelkalar in the ýanýan kamera. The system that is used to prevent the problems caused by these hard accumulation compounds we to expurge hard materials from the senagat gazany is called Boiler Awtomatik düýp üfleme ulgamys

ACCUMULATION (STONE) TYPES

• Calcium carbonate (the most common type of stone), calcium sulfate, silica, phosphate stones, magnesium we magnesium stones, aluminum, iron oxides (usually in the senagat gazany we condensate line is the Önüm of corrosion)

ACCUMULATION EFFECTS

• Reduced thermal conductivity: stones are poor heat conductors we act as insulators as indicated by the various conductivity values. The resulting furring layer causes the reduction of steam generation. In addition, the resulting furring layer increases the fuel consumption we increases the unit cost of steam generation

Temperature build-up in the metal wall: As a stone-coated wall prevents heat transfer, the wall temperature rises. This is called overheating we the metal may lose some of its mechanical properties (elasticity, etc.). These cause local shape disturbances we cause pipe explosion